Abstrakt
The formation and the kinetics of the growth of intermetallic layers between austenitic steel and technically pure aluminum were investigated via SEM analysis of bulk samples after annealing and TEM in-situ annealing. After the first nucleation stage, the total thickness of the intermetallic layer was governed mainly by the parabolic diffusion-controlled growth of the Al5Fe2 phase.